Influence of metal coatings on charging/discharging processes at hydrogenabsorbing alloy electrodes

Abstract

The electrochemical behavior of uncoated and Pdcoated AB¡-type alloy electrodes in alkaline solution was evaluated. Results show that metalcoated alloys with a low Pd content <10 wf/o exhibit fast activation under charge/dis charge cycling and present higher discharge capacities and rate capabilities than the uncoated alloy. The exchange currents per unit of mass for different Pdcoated alloy electrodes were obtained from the slopes of linear polarization curves. For coated alloys with a low Pd con ten t the exchange curren ts are significan tly higher than that for the uncoated alloy. The faster kinetics of hydrogen absorption/desorption processes at Pdcoated alloy electrodes is related to the electrocatalytic effect of Pd on the charge transfer process at the electrode/electrolyte interface, which controls the overall reaction rate.

Se evaluó el comportamiento electroquímico de aleaciones metálicas tipo Al) recubiertas con Pd y sin recubrimiento en solución alcalina. Las aleaciones recubiertas con bajas cantidades de Pd, menores del 10 % en peso, se activan rápidamente bajo ciclado galvanostático y mejoran notablemente las propiedades de carga y descarga respecto a la aleación sin recubrimiento. Las corrientes de intercambio, calculadas a partir de medidas de polarización lineal, son también más altas para las aleaciones recubiertas con bajas cantidades de Pd. La mejoría en la cinética de los procesos de absorción/desorción de hidiógeno en las aleaciones recubiertas se atribuye al efecto electrocatalítico del Pd sobre la reacción de transferencia de carga en la interfase electrodo/electrolito, que determina la velocidad del proceso global.